| Major Characteristics |
Application |
High impact strength
High rigidity
|
Industrial Part
|
| Properties |
Test Method |
Unit |
JH-360FN |
| Melt Flow Rate (MFR) 230º C |
ASTM D 1238 |
g/10min |
20.0 |
| Mold Shrinkage |
HPC Method |
% |
1.4~1.8 |
| Density |
ASTM D 792 |
g/cm³ |
0.90 |
| Tensile Strength at Yield |
ASTM D 638 |
Kg/cm² |
230 |
| Ultimate Elongation |
ASTM D 638 |
% |
>200 |
| Flexural Modulus of Elasticity |
ASTM D 790 |
Kg/cm² |
14,000 |
| Hardness(Rockwell) |
ASTM D 785 |
R |
87 |
| IZOD Impact Strength (23º C) |
ASTM D 256 |
Kg*cm/cm |
11.0 |
| IZOD Imp. Strength (-10º C) |
ASTM D 256 |
Kg*cm/cm |
5.0 |
| DUPONT Imp.Strength (23º C) |
HPC Method |
Kg*cm |
- |
| DUPONT Imp.Strength (-10º C) |
HPC Method |
Kg*cm |
80 |
| Heat Distortion Temperature |
ASTM D 648 |
º C |
120 |
| Above data are not the spec of products, but only for reference |
|