| Major Characteristics |
Application |
High Impact strength
High rigidity
|
High Quality Houseware
Battery Case
Tote Box
|
| Properties |
Test Method |
Unit |
JM-350 |
| Melt Flow Rate (MFR) 230º C |
ASTM D-1238 |
g/10min |
10.0 |
| Mold Shrinkage |
HPC Method |
% |
1.50 |
| Density2 |
ASTM D-1505 |
g/cm³ |
0.9 |
| Tensile Strength at Yield |
ASTM D-638 |
Kg/cm² |
270 |
| Ultimate Elongation |
ASTM D-638 |
% |
>100 |
| Flexural Modulus of Elasticity |
ASTM D-790 |
Kg/cm² |
15,000 |
| Hardness(Rockwell) |
ASTM D-785 |
R |
95 |
| IZOD Impact Strength (23º C) |
ASTM D-256 |
Kg*cm/cm |
8.5 |
| IZOD Imp. Strength (-10º C) |
ASTM D-256 |
Kg*cm/cm |
4.5 |
| DuPont Imp.Strength(-10º C) |
HPC Method |
|
50 |
| Heat Distortion Temperature |
ASTM D-648 |
º C |
115 |
| Mold Shrinkage |
HPC Method |
% |
1.50 |
| Above data are not the spec of products, but only for reference |
|